Bare calite prin inductie si cromate standard – Bare cromate, tevi cromate, bare pentru sisteme hidraulice

Bare calite prin inductie si cromate standard

COMPOZITIE CHIMICA, % DIN GREUTATE

MARCA DE OTEL	C max	Si max	Mn max	P max	S	Ni max	V max
St52(E 355)	0.2	0.5	1.5	0.025	0.02-0.04	–	–
StE 460(E 410)	0.2	0.5	1.7	0.025	max 0.015	0.8	0.2

PROPRIETATI MECANICE (Conform EN 10305-1)

MARCA DE OTEL Conditii de livrare	Rezistenta la rupere Rm	Limita de curgere Rp0.2		Alungire la rupere A5
	– N/mm2 –	-N/mm2 –		– % min –
		Grosime perete ? 16mm	Grosime perete ? 16mm
E 355 +SR	600	520	490	14
E 410 +SR	700	620	620	15
E 355 +N	490-630	355	355	22
E 410 +N	560-730	460	450	22
Diametru exterior	12	16	20	25	28	30	32	35	40	45	50	55	60	63	65	70	75	80	85	90	100	110	120	140
Diametru interior	8	10	14	15	16	15	20	25	20	25	30	35	40	43	45	50	55	60	65	70	80	90	100	120
			15	18		20		20	25	30	35	40	45	53	50	55	60	65	75	75	85	95
				20					30	35	40	45	50		55	60	65	70		80	90

rezistenta la coroziune

Rezultate teste de coroziune AASS si NSS efectuate conform ISO 9227:1990 si evaluate conform ISO 10289:1999.

Diametru (mm)	Min Rating 9 (maxim 0.1% din suprafata cu puncte de coroziune)
<18	72 ore NSS	24 ore AASS
18 la 200	120 ore NSS	40 ore AASS

ISO 9227	ASTM	DIN 50021	Tip ceata salina
NSS	B 117	SS	Neutra
AASS	B 287	ESS	Acetica
CASS	B 368	CASS	Cupro-acetica accelerata

Corespondenta marci otel

EN 10305-1 10305-2	DIN 2391 2393 17179	AFNOR NF-A49310 NF-A49643	B.S. 6323	UNI 7945 7946 663 6403	JIS G3445	ASTM A 513
E355	St52 St52-3	Tu 52b Ts 47a	CEW5-ERW5	Fe 490 Fe 510 D Fe 52-2 Fe 510	STKM 19	1024
E410	StE 460	20MV6	–	–	–	–